Tantalum powder, method for preparing the same, and electrolytic capacitor anode made of the tantalum powder

ABSTRACT

The present invention relates to the tantalum powder and the process for preparing the same, and also relates to the electrolytic capacitor anode made of the tantalum powder. More particularly, the present invention relates to the tantalum powder having a BET surface area not more than 0.530 m 2 /g, Fisher mean particle size not less than 3.00 μm. The present invention relates to the process for preparing the tantalum powder, wherein the tantalum powder is prepared through reducing tantalum compound with a reducing agent, wherein the tantalum powder as seed is added during reduction, and said tantalum powder as seed is the tantalum powder that has been milled.

FIELD OF THE INVENTION

The present invention relates to tantalum powder and the preparation of the same, and also relates to the electrolytic capacitor anode made of the tantalum powder. More particularly, the present invention relates to the improved powder for manufacturing sintered tantalum capacitor anode, and the method for preparing the same.

BACKGROUND OF THE INVENTION

Tantalum powder is usually prepared by means of making a tantalum metal compound reacting with a reducing agent, or hydrogenating and pulverizing the dense metal. Generally, the tantalum powder obtained by means of the former method is porous basic agglomerates having high specific surface area composed of many primary particles, and the tantalum powder obtained by the later method is of high purity, but with low specific surface area.

Typically, sintered tantalum capacitor is made as following steps: compressing tantalum powder to form a pellet, sintering the pellet in a vacuum furnace to form a porous body, subsequently, anodizing the porous body in suitable electrolyte liquid, such as diluted phosphoric acid, to form continuous dielectric oxide film on the surface of the porous sintered body.

Generally, it is desired that an electrolytic capacitor shall have performance characteristics of higher specific capacitance, lower DC leakage and higher breakdown voltage. Since electrolytic capacitor has a lot of useful properties, it has been used in a wide ranging field.

The tantalum powder for manufacturing electrolytic capacitor for high voltage field must have good electric performance, such as higher capacitance and higher breakdown voltage. Usually, for same type of tantalum powder, the larger the specific surface area of the tantalum powder is, the more complex of the particles of the powder are, and the lower the breakdown voltage is. The tantalum powder having poor tolerance of high voltage can hardly be used for high voltage field. The BET surface area of tantalum powder produced by reduction of potassium fluorotantalate with sodium is 0.2˜6.0 m²/g.

In the high voltage tantalum powder field, many researchers have made great efforts for improving the agglomerating performance of tantalum powder, for increasing the capacitance and breakdown voltage of tantalum powder. WO 93/03,191, U.S. Pat. No. 4,740,238, U.S. Pat. No. 5,211,741, U.S. Pat. No. 5,261,942 disclosed improved flake tantalum powder and processes for producing flake tantalum powder, but the processes are complex, difficult to control, and the cost is high, thus the application of these technologies is limited.

Accordingly, there is a need in the prior art for the tantalum powder that can be used in high voltage electrolytic capacitor. Particulary, it is desired that the tantalum powder have high capacitance, excellent performance on DC leakage and good voltage tolerance. Furthermore, it is needed a simple, low cost and easily-controlled process in which tantalum powder with the excellent performance and having high specific capacitance and good tolerance of high voltage can be prepared.

SUMMARY OF THE INVENTION

An object of the present invention is to provide tantalum powder that could be used in high voltage electrolytic capacitor.

Another object of the present invention is to provide tantalum powder with high specific capacitance.

Still another object of the present invention is to provide tantalum powder with excellent performance on DC leakage.

Further object of the invention is to provide tantalum powder having good voltage tolerance.

In order to achieve said objects, the inventors find that, by changing the type of morphology of tantalum powder which is added as seed in the reducing process, the particle morphology of the product tantalum powder and the porosity of the anode can be improved, and thus the properties, including DC leakage and breakdown voltage could be improved, whereby the tantalum powder that can be used in the high voltage electrolytic capacitor is obtained.

Particularly, through one or more of the following various solutions, the present invention realizes one or more of said objects:

(1) Tantalum powder, wherein the tantalum powder has a BET surface area of not more than 0.530 m²/g, and Fisher mean particle size of not less than 3.00 μm. (2) The tantalum powder according to (1), wherein said BET surface area is not more than 0.525 m²/g, preferably not more than 0.520 m²/g, more preferably not more than 0.515 m²/g. (3) The tantalum powder according to (1), wherein said Fisher mean particle size is not less than 3.05 μm, preferably not less than 3.10 μm. (4) The tantalum powder according to (1), wherein said tantalum powder has a particle size distribution such that, the particles of −325 mesh comprise not more than 60 vol % of all particles, preferably not more than 55 vol %, more preferably not more than 50 vol %, further preferably not more than 45 vol %, most preferably not more than 40 vol %. (5) The tantalum powder according to (1), wherein said tantalum powder has an bulk density in a range of 0.5-2.0 g/cm³, preferably 0.5-less than 1.8 g/cm³ (6) The tantalum powder according to any one of (1)-(5), wherein said BET surface area is not less than 0.2 m²/g, preferably not less than 0.3 m²/g, more preferably not less than 0.4 m²/g. (7) The tantalum powder according to any one of (1)-(5), wherein said Fisher mean particle size is not more than 5 μm, preferably not more than 4.5 μm, preferably not more than 4 μm, more preferably not more than 3.5 μm. (8) A process for preparing said tantalum powder according to any one of (1)-(7), wherein the tantalum powder is prepared by reducing tantalum compound with a reducing agent, wherein the tantalum powder as seed is added during reduction, and said tantalum powder as seed is the tantalum powder that has been milled. (9) The process according to (8), wherein the particle size of the tantalum powder as seed is −60 mesh, preferably −100 mesh. (10) The process according to (8), wherein the oxygen content of the tantalum powder as seed is not more than 5000 ppm, preferably not more than 2000 ppm. (11) The process according to (8), wherein the carbon content of the tantalum powder as seed is not more than 40 ppm, preferably not more than 30 ppm. (12) The process according to (8), wherein the nitrogen content of the tantalum powder as seed is not more than 200 ppm, preferably not more than 150 ppm. (13) The process according to (8), wherein the hydrogen content of the tantalum powder as seed is not more than 300 ppm, preferably not more than 150 ppm. (14) The process according to (8), wherein the sum content of iron, nickel and chromium of the tantalum powder as seed is not more than 30 ppm. (15) The process according to (8), wherein said milling is continuous ball-milling for 5-40 hours, preferably for 10-30 hours in a stirring ball mill. (16) The process according to (8), wherein the amount of the tantalum powder as seed added is 5-80 mass % of the theoretical reduction amount of the tantalum powder, preferably 10-70 mass %, more preferably 30-60 mass %. (17) The process according to (8), wherein said process include the following steps:

-   -   (a) mixing tantalum compound with dilution agent and tantalum         powder as seed;     -   (b) adding reducing agent, and reducing the tantalum compound at         a temperature of 700-1000° C.;     -   (c) soaking at a temperature of 700-1000° C.;     -   (d) removing the tantalum powder.         (18) The process according to any one of (8)-(17), wherein said         tantalum compound is at least one selected from of potassium         fluorotantalate, sodium fluorotantalate, or the mixture of them.         (19) The process according to any one of (8)-(17), wherein said         reducing agent is at least one selected from of metal sodium,         potassium or the alloy of them.         (20) The process according to any one of (8)-(17), wherein said         diluent is at least one selected from of sodium chloride,         potassium chloride, potassium fluoride or the mixture of them.         (21) The process according to any one of (8)-(17), wherein said         reduction is carried out at a temperature of 800-1000° C.,         preferably 850-950° C.         (22) The process according to any one of (8)-(17), wherein the         soaking time is 0.5-5 hours, preferably 3-5 hours.         (23) The process according to any one of (8)-(17), wherein the         temperature of soaking is 800-1000° C., preferably 900-950° C.         (24) An electrolytic capacitor anode, wherein said anode is         manufactured from the tantalum powder selected of any one of         (1)-(7).         (25) The electrolytic capacitor anode according to (24), wherein         the specific capacitance is in the range of 6000-30000 μFV/g,         preferably 10000-30000 μFV/g, more preferably 15000-25000 μFV/g.         (26) The electrolytic capacitor anode according to (24), wherein         the energizing voltage is in the range of 100-250V.

BRIEF DESCRIPTION OF THE DRAWING

FIG. 1 shows the SEM photograph at 300 magnifications of the sample I.

FIG. 2 shows a SEM photograph at 500 magnifications of the sample J.

FIG. 3 shows a SEM photograph at 5000 magnifications of the sample I.

FIG. 4 shows a SEM photograph at 5000 magnifications of the sample J.

FIG. 5 shows the porosity of the sintered pellets which are sintered at 1500°/30 min prepared from three different processes.

FIG. 6 shows the porosity of the sintered pellets which are sintered at 1550°/30 min from prepared from three different processes.

DETAILED DESCRIPTION OF THE PRESENT INVENTION

In the present specification, unless otherwise indicated, the unit of ppm indicates “parts per million” in a mass basis; the so-called “high voltage” generally indicates the voltage of 100V or higher, especially 100V-250V.

As used in the present application document and well known to those skill in the art, when using the mesh to express the particle size, the “−” or “+” before the mesh number indicates, respectively, that the particle “pass” or “not pass” the screen mesh of said mesh number, for example, “−60 mesh” indicates that those particles pass the screen mesh of 60 mesh, and accordingly, “+200 mesh” indicates that the particles do not pass the screen mesh of 200 mesh. Hence, the particles of “−60-+200 mesh” refer to the particles pass the screen mesh of 60 mesh, but do not pass the one of 200 mesh.

The parameters for characterizing the particle of the powders include: the BET surface area (m²/g) tested by liquid nitrogen absorption process at low temperature, Fisher mean particle size (FSSS/μm) measured by the Fisher sub-sieve analyzer, the bulk density (SBD,g/cm³) measured by Scott bulk density analyzer, the porosity distribution of the anode measured by the Auto mercury pressure analyzer, the particle size distribution of the powders measured by a laser particle size distribution analyzer, the morphology size of the particle measured by a scan electronic microscope and a transmission electron microscope.

The electrolytic capacitor anode are prepared and characterized as follows: pressing tantalum powder into a pellets according to required density and size; then, sintering the pellet at a required temperature in a vacuum furnace into a sintered pellet; then maintaining the sintered pellet in 0.01 vol % phosphoric acid solution at 80° C. at constant voltage for a certain time period and anodizing the sintered pellet so as to form an electrolytic capacitor anode.

The devices for analyzing the parameters relating to the present invention are as following:

Item Devices Model Manufacture O, N amount Oxygen and LECO LECO CS nitrogen analyzer CS-436 K + Na amount Atom absorb Varian Varian spectrometry 220FS/220Z C amount Carbon, Sulphur LECO LECO CS analyzer CS-406 SBD Bulk density FL4-1 made according analyzer to GB1479-84 CV LCR precise measurer HP-4284A HP BET BET analyzer ASAP2010 Micromerities, USA Porosity Auto mercury AUTOPORE Micromerities, pressure analyzer III 9400 USA Morphology of Scanning electronic JSM-5610LV Japan the particles microscope; Electronics

The results of BET surface area test can reflect the size of primary particles. The finer the primary particle of the tantalum powder is, the larger the BET surface area is, and generally the higher the specific capacitance of the powder is. The Fisher mean particle size is obtained through measuring the speed of air passed a metal tube filled with powder, the Fisher mean particle size value of a powder is associated with the size of particle, meanwhile, it is related to the extent of the agglomerates. For the as-reduced primary powders produced by reduction, the lower the Fisher mean particle size value of the powder is, the larger the surface area is, the higher the specific capacitance is, and the higher the DC leakage is; but for the agglomerated powder, the powders having different specific surface area may be having similar Fisher mean particle size value; and for the powder with same specific capacitance, the powder with higher agglomeration degree have greater Fisher mean particle size value.

According to the present invention, said tantalum powder is that used for electrolytic capacitor with the energizing voltage of 100V ˜250V.

According to the present invention, there is no specific limitation on the tantalum powder as seed, as long as it can be added in the reduction process as seed. In a preferred embodiment of the present invention, said tantalum powder as seed (i.e. the milled tantalum powder) has the properties as follows: particle size of −60 mesh, preferably of −100 mesh; the oxygen content of not more than 5000 ppm, preferably not more than 2000 ppm; the carbon content of not more than 40 ppm, preferably not more than 30 ppm; the nitrogen content of not more than 200 ppm, preferably not more than 150 ppm; the hydrogen content of not more than 300 ppm, preferably of not more than 150 ppm; the sum contents of iron, nickel and chromium of not more than 30 ppm.

In the present invention, there is no specific limitation on the process for preparing tantalum powder as seed, but preferably, the tantalum powder as seed is that has been milled. In a preferred embodiment of the present invention, said tantalum powder as seed has been continuously ball-milled for 5-40 hours with a stirring ball-mill.

Preferably, the milling process may include: the start material is stirring ball-milled in a stirring ball mill, with alcohol as the milling medium, to form a flake powder having the aspect ratio of 5-20, then, the impurities in the milled powder are removed by leaching. Said aspect ratio indicates the ratio of the width to thickness of a particle. The aspect ratio can be tested with a scanning electronic microscope. For instance, the aspect ratio can be reliably obtained in this way: dispersing the particles and sticking them solidly to an adhesive tape, observing with a scanning electronic microscope, and testing the radial length and thickness of 2000-3000 particles, calculating the average value of radial length to thickness of these particles.

According to the process of the present invention, the tantalum powders with larger particle size and lower specific surface area can be obtained by adding tantalum powder as seed without changing the system and condition of the process. Hence, the resultant tantalum powder has good sintering-properties, as well as high capacitance at high temperature, high breakdown voltage, low DC leakage and good agglomerating performance. Therefore, the tantalum powder according to the present invention is particularly useful in high voltage electrolytic capacitor.

According to the process of the present invention, there is no specific limitation on the addition amount of the tantalum powder as seed, so long as it's the amount suffices for acting as a seed. In a preferred example of the present invention, said addition amount of the tantalum powder as seed is 5-80 mass % of the theoretical reduction weight, preferably 10-70 mass %, more preferably 30-60 mass %. The so called “the theoretical reduction weight” means the weight of the tantalum powder that can be obtained by the present invention according to theoretical calculation, and which includes the amount of tantalum powder obtained from the reduction and the amount of tantalum powder added as seed. In the present application, all the percentage relating to the amount of tantalum powder as seed were of the above-said meaning.

Moreover, so called “without changing the system and condition of the process” indicates that the tantalum powder is prepared based on conventional process, that is, tantalum metal is prepared by reducing tantalum compound with a reducing agent without changing any process condition. Said process is known to those skilled in the art. According to the present invention, the parameters of the process are not specially limited.

It is to be understand that the following description of preferred embodiments by way of examples in conjunction with accompanying drawings are provided only to illustrate the features and the advantages of the present invention and not to limit the scope of the appended claims.

In the following examples, the sample tantalum powder are prepared with the following process, wherein:

(a) For sample A, D and H: mixing and charging an amount of 150 kg of K₂TaF₇ and 160 kg of diluent salt of KCl into a reaction vessel;

-   -   for sample B, C, E, F, I and J, the above 150 Kg of K₂TaF₇ is         partially replaced by the tantalum powder as seed with the         amount of tantalum unchanged, and the type of the diluent salt         and its addition amount remain unchanged, afterward they are         mixed and charged into a reaction vessel;         (b) After charging, heating the charged reaction vessel to 920°         C., steadily injecting liquid sodium into the reaction vessel to         carry out the reduction under stirring with the stirring rate         controlled at 80 revolutions per minute, and the reaction         temperature is regulated by controlling the speed of injecting         sodium;         (c) soaking at the temperature of 920° C. for 0.5-5 hours, at         the end of injecting sodium;         (d) removing the powders from the furnace after cooling, and         said sample tantalum powders are obtained.

In the following examples, the tantalum powder as seed is referred as “seed tantalum powder” for short. The seed tantalum powder has the following characteristics: particle size of −100 mesh; 4750 ppm of oxygen content; 35 ppm of carbon content; 170 ppm of nitrogen content; 260 ppm of hydrogen content; and the 25 ppm of the sum contents of iron, nickel and chromium. Please note that, in the following examples, no all the samples are in the scope of the present invention. For convenient comparison, the applicant put the samples according the present invention and the samples not according to the present invention into the same example. Particularly, samples A, D and H are the tantalum powders out of the scope of the present invention (in other words, without the addition of the seed powder in the process), and the sample B, C, E, F, I and J are in the scope of the present invention (in other words, with the addition the seed powder in the process).

Example 1

Sample A (not according to the present invention): obtained directly by sodium reduction;

Sample B (according to the present invention): obtained with addition of 10 mass % seed tantalum powder in the reduction;

Sample C (according to the present invention): obtained with addition of 20 mass % seed tantalum powder in the reduction.

TABLE 1 Specific surface area, bulk density and Fisher mean particle size of the samples A, B and C Specific surface Bulk density Fisher mean particle Sample area (cm²/g) (g/cm³) size (μm) A 0.5328 1.84 3.05 B 0.5120 1.78 3.15 C 0.4875 1.76 3.12

TABLE 2 The distribution of the particle size of the samples A, B and C (all percentages are expressed by vol. %, same hereinafter) Sample +60(%) −60/+200(%) −200/+325(%) −325/+400(%) −400(%) A 0.46 27.58 10.42 15.86 45.68 B 0.36 28.12 12.32 13.46 45.74 C 0.48 30.26 15.46 13.88 39.92

An amount of 0.5 g of the tantalum powder from Samples A, B and C were respectively pressed into pellets having a density of 5.0 g/cm³. The pellets were sintered in a vacuum furnace at a pressure of 10⁻³ Pa, at different temperatures of 1450° C., 1500° C., 1550° C. and 1600° C. for 30 minutes to form sintered pellets. Said sintered pellets were energized in 0.01 vol % phosphoric acid solution at 100V voltages to form electrolytic capacitor anodes. The properties were measured, and the results are listed in Table 3, 4 and 5.

TABLE 3 The specific capacitance of the electrolytic capacitor anodes from the samples A, B and C sintered at various sintering conditions. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min A 25680 23060 17328 13436 B 25565 22140 18510 13725 C 25326 20100 17680 14015

TABLE 4 The DC leakage of the electrolytic capacitor anodes from the sample A, B and C sintered at various sintering conditions 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min A 0.42 0.18 0.21 0.32 B 0.38 0.17 0.19 0.30 C 0.37 0.17 0.18 0.28

TABLE 5 The shrinkage of the electrolytic capacitor anodes from the samples A, B and C sintered at various sintering conditions. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min A 7.4 9.6 10.8 14.8 B 6.8 9.4 10.6 15.4 C 5.5 7.8 8.4 11.4

Example 2

Sample D (not according to the present invention): obtained directly by sodium reduction

Sample E (according to the present invention): obtained with addition of 30 mass % seed tantalum powder in the reduction

Sample F (according to the present invention): obtained with addition of 50 mass % seed tantalum powder in the reduction

TABLE 6 The specific surface area, bulk density and Fisher mean particle size of the samples D, E and F. Specific surface area bulk density Fisher mean particle size Sample (cm²/g) (g/cm³) (μm) D 0.5238 1.82 2.90 E 0.4662 1.68 3.30 F 0.4584 1.63 3.35

TABLE 7 The particle size distribution of the samples D, E and F. Sample +60(%) −60/+200(%) −200/+325(%) −325/+400(%) −400(%) D 0.56 26.62 10.86 16.42 45.54 E 0.62 30.12 22.32 12.80 34.14 F 0.36 31.86 21.46 13.20 33.12

An amount of 0.5 g of the tantalum powder from samples D, E and F were respectively pressed into pellets having density of 5.0 g/cm³. The pellets were sintered in a vacuum furnace at a pressure of 10⁻³ Pa, at different temperatures of 1450° C., 1500° C., 1550° C. and 1600° C. for 30 minutes to form a sintered pellets. Said sintered pellets were energized in 0.01 vol % phosphoric acid solution at 100V voltages to form electrolytic capacitor anodes. The properties were measured, and the results are listed in Table 8, 9 and 10.

TABLE 8 The specific capacitance of the electrolytic capacitor anodes from the samples D, E and F sintered at various sintering conditions and energized at 100 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min D 25700 22980 17160 13360 E 24875 23120 18236 15238 F 24207 23740 19508 16848

TABLE 9 The DC leakage of the anodes from the samples D, E and F sintered at various sintering conditions and energized at 100 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min D 0.40 0.17 0.21 0.32 E 0.35 0.16 0.18 0.26 F 0.32 0.16 0.18 0.22

TABLE 10 The shrinkage of the anodes from the samples D, E and F sintered at various sintering conditions and energized at 100 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min D 5.0 20.1 28.2 36.7 E 3.0 12.6 16.2 28.6 F 2.0 7.4 11.3 23.2

An amount of 0.5 g of said samples D, E and F were respectively pressed into pellets having density of 5.0 g/cm³. The pellets were sintered in a vacuum furnace at a pressure of 10⁻³ Pa, at different temperatures of 1450° C., 1500° C., 1550° C. and 1600° C. for 30 minutes to form sintered pellets. Said sintered pellets were energized in 0.01 vol % phosphoric acid solution at 160V voltages to form electrolytic capacitor anodes. The properties were measured, and the results are listed in Table 11, 12 and 13.

TABLE 11 The specific capacitance of the electrolytic capacitor anodes from the samples D, E and F sintered at various sintering conditions and energized at 160 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min D 23700 18600 15120 12980 E 21980 19800 17680 14960 F 22340 20400 18150 15200

TABLE 12 The DC leakage of the electrolytic capacitor anodes from the samples D, E and F sintered at various sintering conditions and energized at 160 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min D 0.52 0.35 0.31 0.32 E 0.41 0.29 0.28 0.27 F 0.32 0.27 0.25 0.25

TABLE 13 The shrinkage of the anodes from the samples D, E and F sintered at various sintering conditions and energized at 160 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min D 4.3 15.4 20.6 28.6 E 2.1 6.8 12.4 21.5 F 1.8 5.9 9.8 18.6

Example 3

Sample H (not according to the present invention): obtained directly by sodium reduction

Sample I (according to present invention): obtained with addition of 50 mass % seed tantalum powder in the reduction

Sample J (according to present invention): obtained with addition of 70 mass % seed tantalum powder in the reduction

TABLE 14 The specific surface area, apparent density and Fisher mean particle size of the samples H, I and J. surface area bulk density Fisher mean particle size Sample (cm²/g) (g/cm³) (μm) H 0.5348 1.80 2.98 I 0.4568 1.66 3.28 J 0.4532 1.60 3.30

TABLE 15 The particle size distributions of the samples H, I and J (vol. %). Sample +60 −60/+200 −200/+325 −325/+400 −400 H 0.56 25.52 11.38 14.98 47.56 I 0.36 30.98 24.66 11.88 32.12 J 0.52 32.86 27.52 10.24 28.86

An amount of 0.5 g of said powder samples H, I and J were respectively pressed into pellets having density of 5.0 g/cm³. The pellets were sintered in a vacuum furnace at a pressure of 10⁻³ Pa, at different temperatures of 1450° C., 1500° C., 1550° C. and 1600° C. for 30 minutes to form sintered pellets. Said sintered pellets were energized in 0.01 vol % phosphoric acid solution at 160V voltages to form electrolytic capacitor anodes. The properties were measured, and the results are listed in Table 16, 17 and 18.

TABLE 16 The specific capacitance of the electrolytic capacitor anodes from the samples H, I and J sintered at various sintering conditions and energized at 160 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min H 23460 17580 14420 12650 I 21320 19620 17330 15180 J 20380 20560 17650 15210

TABLE 17 The DC leakage of the electrolytic capacitor anodes from the samples H, I and J sintered at various sintering conditions and energized at 160 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min H 0.66 0.46 0.36 0.35 I 0.48 0.28 0.27 0.26 J 0.36 0.28 0.26 0.24

TABLE 18 The shrinkage of the electrolytic capacitor anodes from the samples H, I and J sintered at various sintering conditions and energized at 160 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min H 4.8 15.8 18.6 27.4 I 2.0 6.2 10.2 17.8 J 0.8 5.6 9.4 16.6

An amount of 0.5 g of tantalum powder from sample I, J and H were respectively pressed into pellets having a density of 5.0 g/cm³. The pellets were sintered in a vacuum furnace at a pressure of 10⁻³ Pa, at different temperatures of 1450° C., 1500° C., 1550° C. and 1600° C. for 30 minutes to form sintered pellets. Said sintered pellets were anodized in 0.01 vol % phosphoric acid solution at 200V voltages to form electrolytic capacitor anodes. The properties were measured, and the results are listed in Table 19, 20 and 21.

TABLE 19 The specific capacitance of the electrolytic capacitor anodes from the samples H, I and J sintered at various sintering conditions and energized at 200 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min H 17652 15420 12180 10250 I 17180 17230 15830 14360 J 17268 17280 15850 14380

TABLE 20 The DC leakage of the electrolytic capacitor anodes from the samples H, I and J sintered at various sintering conditions and energized at 200 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min H 1.32 0.76 0.52 0.40 I 0.86 0.42 0.36 0.32 J 0.82 0.40 0.36 0.30

TABLE 21 The shrinkage of the electrolytic capacitor anodes from the samples H, I and J sintered at various sintering conditions and energized at 200 V. 1450° C./ 1500° C./ 1550° C./ 1600° C./ Sample 30 min 30 min 30 min 30 min H 4.8 15.8 18.6 27.4 I 2.0 6.2 10.2 17.8 J 0.8 5.6 9.4 16.6

As described above, the tantalum powder according to the present invention has proper bulk density. The tantalum powder according to the present invention has better agglomerating effect and substantially lower ratio of fine particles, comparing with those in the prior art. Particularly, the particles of −325 mesh only comprise not more than 60 vol % of all particles. The electrolytic capacitor anodes manufactured from the tantalum powder, at high energizing voltage, has comparative or even higher specific capacitance and lower leakage, and has improved sintering performance (shrinkage). Thus, it can be seen that the tantalum powder according to the present invention especially suitable for high voltage electrolytic capacitor. Moreover, as can be seen by comparing the samples F and I, which are prepared under the identical process parameters, the process according to the present invention has excellent reproducibility which is very advantageous for the practice.

Other embodiments of the present invention will be apparent to those skilled in the art from consideration of the specification and practice of the present invention disclosed herein. It is intended that the specification and examples be considered as exemplary only, with a true scope and spirit of the present invention being indicated by the following claims. 

1. Tantalum powder, wherein the tantalum powder has a BET surface area of not more than 0.530 m²/g, and Fisher mean particle size of not less than 3.00 μm.
 2. The tantalum powder according to claim 1, wherein said BET surface area is not more than 0.525 m²/g.
 3. The tantalum powder according to claim 2, wherein said BET surface area is not more than 0.520 m²/g
 4. The tantalum powder according to claim 1, wherein said Fisher mean particle size is not less than 3.05 μm.
 5. The tantalum powder according to claim 4, wherein said Fisher mean particle size is not less than 3.10 μm
 6. The tantalum powder according to claim 1, wherein said tantalum powder has a particle size distribution such that, the particles of −325 mesh comprise not more than 60 vol % of all particles.
 7. The tantalum powder according to claim 6, wherein said tantalum powder has a particle size distribution such that, the particles of −325 mesh comprise not more than 55 vol % of all particles.
 8. The tantalum powder according to claim 7, wherein said tantalum powder has a particle size distribution such that, the particles of −325 mesh comprise not more than 50 vol % of all particles.
 9. The tantalum powder according to claim 1, wherein said tantalum powder has an bulk density in a range of 0.5-2.0 g/cm³.
 10. A process for preparing the tantalum powder according to claim 1, wherein the tantalum powder is prepared by reducing tantalum compound with a reducing agent, wherein the tantalum powder as seed is added during reduction, and said tantalum powder as seed is the tantalum powder that has been milled.
 11. The process according to claim 10, wherein the particle size of the tantalum powder as seed is −60 mesh.
 12. The process according to claim 10, wherein said milling is continuous ball-milling for 5-40 hours, preferably for 10-30 hours in a stirring ball mill.
 13. The process according to claim 10, wherein the amount of the tantalum powder as seed added is 5-80 mass % of the theoretical reduction amount of the tantalum powder.
 14. The process according to claim 13, wherein the amount of the tantalum powder as seed added is 10-70 mass % of the theoretical reduction amount of the tantalum powder.
 15. The process according to claim 14, wherein the amount of the tantalum powder as seed added is 30-60 mass % of the theoretical reduction amount of the tantalum powder
 16. The process according to claim 10, wherein said process include the following steps: (a) mixing tantalum compound with dilution agent and tantalum powder as seed; (b) adding reducing agent and reducing tantalum compound at a temperature of 700-1000° C.; (c) soaking at a temperature of 700-1000° C.; (d) removing the tantalum powder.
 17. An electrolytic capacitor anode, wherein said anode is manufactured from the tantalum powder of claim
 1. 18. The electrolytic capacitor anode according to claim 17, wherein the specific capacitance is in the range of 6000-30000 μFV/g.
 19. The electrolytic capacitor anode according to claim 18, wherein the specific capacitance is in the range of 10000-30000 μFV/g.
 20. The electrolytic capacitor anode according to claim 17, wherein the energizing voltage is in the range of 100-250V. 